1. An electric lamp comprising
a light-transmitting lamp vessel (1),
an electric element (2) in the lamp vessel (1),
current supply conductors (4, 5) extending to the electric element (2),
a lamp cap (6) connected to the lamp vessel (1), which lamp cap (6) has a shell portion (7) and a base portion (8) which each support an electric contact member (9), each electric contact member (9) having a surface on which the respective current supply conductor is fastened by means of a solidified connection body (10) comprising aluminum and an additive,
characterized in that said additive comprises 5 to 16% by weight of silicon.
2. An electric lamp as claimed in claim 1, characterized in that said additive comprises 11 to 13.5% by weight of silicon.
3. An electric lamp as claimed in claim 1, characterized in that the connection body (10) comprises a eutectic mixture of aluminum with approximately 12.5% by weight of silicon.
The claims below are in addition to those above.
All refrences to claim(s) which appear below refer to the numbering after this setence.
1. A method for preparing a fibrous silver-based electrical contact material, comprising following steps of:
(1) uniformly mixing reinforcement powder and matrix silver powder to obtain a mixture, and loading the mixture into a high power ball mill for ball grinding, wherein the reinforcement powder and the matrix silver powder are mixed according to a predetermined weight ratio by which silver coats on the reinforcement powder to form coated bodies and aggregates of the coated bodies are obtained after the high power ball grinding;
(2) pouring a composite powder body, namely the aggregates of the coated bodies obtained from the step (1), and the matrix silver powder into a powder mixing machine to mix, wherein a weight ratio of the composite powder body to the matrix silver powder is counted according to constituents of desired preparation materials and a predetermined fiber size, and then obtaining a powder body;
(3) processing the powder body obtained from the step (2) with cold isostatic pressing to obtain a green body;
(4) sintering the green body obtained by the cold isostatic pressing;
(5) processing the green body obtained by the sintering, with hot pressing;
(6) processing the green body obtained by the hot pressing, with hot extruding, and generating a fibrous silver-based electrical contact material.
2. The method, as recited in claim 1, wherein the step (1) adopts the silver powder having a particle size between 100 meshes and 400 meshes.
3. The method, as recited in claim 2, wherein the step (1) adopts the reinforcement powder of any material as along as the reinforcement powder are coated with silver after the reinforcement powder and the silver powder are processed with high power ball grinding; the reinforcement material is made of one material or a mixture of more than one material.
4. The method, as recited in claimer 1, wherein, in the step (1), a weight ratio of the reinforcement powder to the silver powder is between 0.5and 3; the ball mill rotates at a speed between 180 rpm and 280 rpm; the ball grinding last for 5 hours to 12 hours.
5. The method, as recited in claim 3, wherein, in the step (1), a weight ratio of the reinforcement powder to the silver powder is between 0.5 and 3; the ball mill rotates at a speed between 180 rpm and 280 rpm; the ball grinding last for 5 hours to 12 hours.
6. The method, as recited in claim 1, wherein, in the step (2), the weight ratio of the composite powder body and the matrix silver powder is between 1 and 0.136; the powder mixing machine rotates at a speed between 20 rpm and 30 rpm; the powder mixing lasts for 2 hours to 4 hours.
7. The method, as recited in claim 5, wherein, in the step (2), the weight ratio of the composite powder body and the matrix silver powder is between 1 and 0.136; the powder mixing machine rotates at a speed between 20 rpm and 30 rpm; the powder mixing lasts for 2 hours to 4 hours.
8. The method, as recited in claim 1, wherein the step (3) comprises the cold isostatic pressing under a cold isostatic pressure between 100 MPa and 500 MPa.
9. The method, as recited in claim 7, wherein the step (3) comprises the cold isostatic pressing under a cold isostatic pressure between 100 MPa and 500 MPa.
10. The method, as recited in claim 1, wherein the step (4) comprises the sintering; a sintering temperature is between 600\xb0 C. and 900\xb0 C. and the sintering lasts for 5 hours to 9 hours.
11. The method, as recited in claim 9, wherein the step (4) comprises the sintering; a sintering temperature is between 600\xb0 C. and 900\xb0 C. and the sintering lasts for 5 hours to 9 hours.
12. The method, as recited in claim 1, wherein the step (5) comprises the hot pressing; a hot pressing temperature is between 500\xb0 C. and 900\xb0 C.; a hot pressing pressure is between 300 MPa and 700 MPa; the hot pressing lasts for 1 min to 30 min.
13. The method, as recited in claim 11, wherein the step (5) comprises the hot pressing; a hot pressing temperature is between 500\xb0 C. and 900\xb0 C.; a hot pressing pressure is between 300 MPa and 700 MPa; the hot pressing lasts for 1 min to 30 min.
14. The method, as recited in claim 1, wherein the step (6) comprises the hot extruding; the green body is heated under a temperature between 600\xb0 C. and 900\xb0 C.; an extrusion ratio is between 20 and 400; an extrusion speed is between 5 cmmin and 20 cmmin; a pre-heating temperature of extruding moulds is between 300\xb0 C. and 500\xb0 C.
15. The method, as recited in claim 13, wherein the step (6) comprises the hot extruding; the green body is heated under a temperature between 600\xb0 C. and 900\xb0 C.; an extrusion ratio is between 20 and 400; an extrusion speed is between 5 cmmin and 20 cmmin; a pre-heating temperature of extruding moulds is between 300\xb0 C. and 500\xb0 C.
16. A fibrous silver-based electrical contact material produced by the method as recited in claim 1, wherein said fibrous silver-based electrical contact material has an obvious fibrous reinforcement material, wherein a fibrous structure of said reinforcement material is formed by particles thereof arranged along a predetermined direction; powder particles of said fibrous reinforcement material have an average size of 5 nm to 30 \u03bcm; said powder particles can be of any material as along as said powder particles are coated with silver after said powder particles and silver powder are processed with high power ball grinding; and said reinforcement material can be made of one material or a mixture of more than one material.
17. A fibrous silver-based electrical contact material produced by the method as recited in claim 15, wherein said fibrous silver-based electrical contact material has an obvious fibrous reinforcement material, wherein a fibrous structure of said reinforcement material is formed by particles thereof arranged along a predetermined direction; powder particles of said fibrous reinforcement material have an average size of 5 nm to 30 \u03bcm; said powder particles can be of any material as along as said powder particles are coated with silver after said powder particles and silver powder are processed with high power ball grinding; and said reinforcement material can be made of one material or a mixture of more than one material.